Escorene™ Ultra FL 01418
| Category: | EVA , Ethylene Vinyl Acetate Copolymer Resin |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | Escorene™ Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NK5U2k_Escorene-Ultra-FL-01418.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FL 01418 is mainly designed for high speed/low coating extrusion coating, and is a good coextrusion component that can be matched with other polymers. FL 01418 is an excellent heat sealing material with extremely low sealing temperature and high transparency. Good extrusion coating effect can be obtained at 225°C (437 °F) under processing conditions. Processing temperatures above 240°C (464 °F) may cause resin degradation. FL01418 should be put into the extruder after low density polyethylene with similar or higher melt index. The machine should be thoroughly cleaned with low density polyethylene or suitable detergent before stopping. |
| General Information | |
|---|---|
| Additive |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vinyl Acetate Content | 18.0 | wt% | ExxonMobil Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 87 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 39.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 100 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 51.0 | °C | ASTM D1525 |
| Legal statement |
|---|
| 有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用 |
| Extrusion instructions |
|---|
| Excellent results are obtained in extrusion coating at 225°C (437°F) temperature range. Processing temperatures above 240°C (464°F) may cause resin degradation. FL01418 should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown. |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 612MK46 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| SHIN-A SCP-240A75 | SHIN-A T&C | Epoxy | SHIN-A |
| TOTAL Polypropylene PPH 3860X | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Ecodear® Prototype - High PLA Content | Toray Resin Company | PLA | Ecodear® |
| Kepex® 3330GFS | Korea Engineering Plastics Co., Ltd | PBT | Kepex® |