| TRANSMARE® 70CNF30-0.005 is a 30% bamboo fiber reinforced polypropylene copolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 6.0 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 24 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm) | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 4.00 mm, Injection Molded) | 28.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 4.00 mm, Injection Molded) | 2.2 | % | ISO 527-2/50 |
| Flexural Modulus | 2750 | MPa | ISO 178 |
| Flexural Stress | 42.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C | 2.2 | kJ/m² | ISO 179/1A |
| 23°C | 3.6 | kJ/m² | ISO 179/1A |
| Charpy Unnotched Impact Strength | ISO 179/1U | ||
| -40°C | 8.0 | kJ/m² | ISO 179/1U |
| 23°C | 11 | kJ/m² | ISO 179/1U |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | 2.2 | kJ/m² | ISO 180/1A |
| 23°C | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -40°C | 9.3 | kJ/m² | ISO 180/1U |
| 23°C | 10 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 71.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 155 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 165 | °C | |
| Middle Temperature | 175 | °C | |
| Front Temperature | 185 | °C | |
| Nozzle Temperature | 190 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| In specific cases pre-drying of this material might be required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene MCHPMI20 | Rainmaker Polymers LLC | PP Homopolymer | Rainmaker Polypropylene |
| TAIRILAC AG12AJ | Formosa Plastics Corporation | ABS | TAIRILAC |
| VYLOPET® EMC310 | TOYOBO America, Inc. | PC+PBT | VYLOPET® |
| OXPEKK® IG240C | Oxford Performance Materials, Inc. | PEKK | OXPEKK® |
| Sylvin 8220-67 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |