Eraclene® BC 82 L
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Eraclene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NHgmMg_Eraclene-BC-82-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eraclene BC 82 L is a high density polyethylene resin (HDPE), with antioxidants, suitable for blow moulding application. It is especially recommended for the production of containers up to 20 liters. Eraclene BC 82 L combines a very good stress cracking resistance with a good rigidity and impact strength. This resin exhibits a high melt strength together with a moderate swelling. Eraclene BC 82 L is characterized by an intermediate molecular weight distribution which balances overall performances with ease of processing. Main Application Eraclene BC 82 L is used to produce, with high-speed machines, blow moulded containers for household and industrial chemicals (detergents, bleaches, etc), cosmetics (shampoos, creams, lotions, etc.), health and medical aids. Eraclene BC 82 L is suitable for thin wall items and can be extruded into profiles and sheets. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.951 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.25 | g/10 min | |
| 190°C/5.0 kg | 0.90 | g/10 min | |
| Environmental Stress-Cracking Resistance (Compression Molded) | > 150 | hr | ISO 22088 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Compression Molded | 26.0 | MPa | |
| Break, Compression Molded | 30.0 | MPa | |
| Tensile Strain (Break, Compression Molded) | > 600 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1(Compression Molded) | 180 | J/m | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 123 | °C | ISO 306/A |
| Melting Temperature | 134 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS PCA-1012 | Polymer Technology and Services, LLC | PC+ABS | PTS |
| Reon 57GMR01 | Reliance Industries Limited | PVC Homopolymer | Reon |
| Moplen 2152HOXP | LyondellBasell Industries | PP Homopolymer | Moplen |
| Borealis PE LE0563 | Borealis AG | PE, Unspecified | Borealis PE |
| Braskem EVA VA8010SUV | Braskem | EVA | Braskem EVA |