POLYFLAM® RPP 2120
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NHT2UV_POLYFLAM-RPP-2120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% mineral filled flame retardant PP-homopolymer, halogen free according to DIN VDE 0472 part 815 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 2.0 | kJ/m² | ISO 179/1eA |
| 23°C | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 16 | kJ/m² | ISO 179/1eU |
| 23°C | 80 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 94.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 51.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ISO 306/A50 |
| -- | 94.0 | °C | ISO 306/B50 |
| Ball Pressure Test (140°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | V-2 | IEC 60695-11-10, -20 | |
| 1.60 mm | V-2 | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 700 | °C | IEC 60695-2-13 |
| 1.50 mm | 700 | °C | IEC 60695-2-13 |
| 3.00 mm | 700 | °C | IEC 60695-2-13 |
| Oxygen Index | 26 | % | ISO 4589-2 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 220 | °C | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 80.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 40.0 - 90.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Cushion | < 5.00 | mm | |
| Screw Speed | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Y1200 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| FM® 300-2 | Cytec Industries Inc. | Adhesive | FM® |
| HI-ZEX™ 232J | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| Karina BLACK PVC COMPOUND 909D48/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SQUARE® SSR8630-30AF/BF | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |