LNP™ COLORCOMP™ R1000S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NHED5Z_LNP-COLORCOMP-R1000S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP* R1000S is an unfilled Nylon 66. Added features of this material is: Heat Stabilized. Also known as: LNP* COLORCOMP* Compound R-1000 HS Product reorder name: R1000S |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.22 | g/cm³ | ASTM D792 |
| -- | 1.23 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2 |
| Flexural Modulus | 3200 | MPa | ISO 178 |
| Flexural Stress | 11.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2(1.8 MPa, Unannealed, 64.0 mm Span) | 75.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 254 to 266 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 60.0 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 A X 108950 D | RTP Company | Nylon 6 | RTP |
| Scolefin 35 G 10-9 | Ravago Group | PP Homopolymer | Scolefin |
| TAISOX 3490 | Formosa Plastics Corporation | LLDPE | TAISOX |
| HiFill® TPU GF40 | Techmer Engineered Solutions | TPU, Unspecified | HiFill® |
| Huafon T25 | Huafon Group Co., Ltd. | Nylon 66 | Huafon |