RTP 2700 S-60A MD
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NGw7ov_RTP2700S60AMD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ISO 10993 Tested |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.890 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.6 - 2.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 60 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain, 3.18 mm) | 1.79 | MPa | ASTM D412 |
| Tensile Strength 2(Break, 3.20 mm) | 8.27 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 700 | % | ASTM D412 |
| Tear Strength 4 | 33.3 | kN/m | ASTM D624 |
| Compression Set 5 | ASTM D395B | ||
| 23°C, 22 hr | 21 | % | ASTM D395B |
| 70°C, 22 hr | 46 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 77 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 177 - 204 | °C | |
| Mold Temperature | 16 - 38 | °C |
| Note Message | |
|---|---|
| 1 . | C mold, 510mm/min |
| 2 . | C mold, 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | C mould |
| 5 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND 1000 BK06 | POLY GIN | PC | MARCOBLEND |
| Topolymer® 5321-951E | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| NOVADURAN® SEF-530 | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| AFFINITY™ PL 1845G | The Dow Chemical Company | POP | AFFINITY™ |
| 3M™ Dyneon™ PTFE Compound TF 8390 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |