MonoSol® M1030 38µ
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | MonoSol, LLC |
| Trademark: | MonoSol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NGUvDR_MonoSol-M1030-38-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MonoSol M1030 is a PVOH based thermoplastic film, soluble in hot water and manufactured using MonoSol's proprietary solution cast technology. MonoSol M1030 is a hot water-soluble general purpose PVOH film. With high elongation, M1030 performs well in molding and vacuum bag operations. The maximum use temperature is 275 F (135 C). Standard thicknesses are 38 micron (1.5 mil), 51 micron (2.0 mil) and 76 micron (3.0 mil). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Moisture Content (23°C, 38.1 µm) 1 | 6.0 | wt% | |
| Solubility 2 | |||
| Disintegration : 60°C, 38.1 µm | 10.0 | sec | |
| Dissolution : 60°C, 38.1 µm | 32.0 | sec |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yield (23°C, 38.1 µm) 3 | 20.6 | m²/kg | |
| Film Thickness - Tested | 38 | µm | |
| Film Thickness - Recommended / Available | 38 µm, 51 µm, and 76 µm | ||
| Secant Modulus | |||
| 10%, MD : 38 µm | 57.9 | MPa | ASTM D882 |
| 100%, MD : 38 µm | 10.3 | MPa | ASTM D882 |
| 10%, MD : 23°C, 38 µm | 57.9 | MPa | ISO 527-3 |
| 100%, MD : 23°C, 38 µm | 10.3 | MPa | ISO 527-3 |
| Tensile Strength - MD | |||
| Break, 38 µm | 21.4 | MPa | ASTM D882 |
| 23°C, 38 µm | 21.4 | MPa | ISO 527-3 |
| Tensile Elongation - MD | |||
| Break, 38 µm | 360 | % | ASTM D882 |
| Break, 23°C, 38 µm | 360 | % | ISO 527-3 |
| Elmendorf Tear Strength - MD | |||
| 38 µm | 1100 | g | ASTM D1922 |
| 38 µm | 0.11 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Continuous Use Temperature | 135 | °C |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| 3 . | density at 1.28 g/cc |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-50138D | Teknor Apex Company | TPE | Medalist® |
| Borealis PE VS4580 | Borealis AG | HDPE | Borealis PE |
| Chiao Fu PBT PBT312G30 BK | Chiao Fu Enterprises Co., Ltd. | PBT | Chiao Fu PBT |
| EverGlide® SG3230 | Polymer Dynamix | PEEK | EverGlide® |
| Leona™ 90G60 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |