LNP™ THERMOCOMP™ KF008 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NFYkaS_LNP-THERMOCOMP-KF008-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP KF008 is a compound based on Acetal Copolymer resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound KFX-1008 Product reorder name: KF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.30 to 0.70 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 3.0E-3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 131 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 9600 | MPa | ISO 178 |
| Flexural Stress | 179 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 165 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 164 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 4.2E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 8.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ C16USQM42 | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| Sasol Polymers PP CMR648 | Sasol Polymers | PP Impact Copolymer | Sasol Polymers PP |
| Novalloy-B B27B6 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |
| Elastron® D D400.A35.N | Elastron USA, Inc. | SBS | Elastron® D |
| PHOENIX™ 13551 | Phon Tech Industrial Company | TPE | PHOENIX™ |