Cellophane™ XS440
| Category: | Cellulose, Regenerated , Regenerated Cellulose |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Cellophane™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NFBPC0_Cellophane-XS440.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Regenerated cellulose film (RCF), coated on both sides with polyvinylidene (PVdC) copolymer by a solvent process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.20 | ||
| vs. Itself - Static | 0.25 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 31 µm | > 3000 | MPa | |
| 1% Secant, TD : 31 µm | > 1500 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 31 µm | 125 | MPa | |
| TD : Yield, 31 µm | 70.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 31 µm | 22 | % | |
| TD : Break, 31 µm | 70 | % | |
| Seal Strength 1 | 2.2 | N/mm | Internal Method |
| Seal Initiation Temperature 2(31 µm) | 100 to 160 | °C | Internal Method |
| Oxygen Transmission Rate (Wet) 3(23°C, 31 µm, 0.0% RH) | 3.00 | cm³/m²/24 hr | ASTM F1927 |
| Water Vapor Transmission 4 | 10 | g/m²/24 hr | ASTM E96 |
| Film Gauge | 30.6 | µm | Internal Method |
| Yield (30.6 µm) | 22.7 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.6 µm) | 105 | ASTM D2457 | |
| Haze 5(30.6 µm) | 4.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | g(f)/38mm, 135°C, 0.5 secs, 69 kN/m² |
| 2 . | 0.5s dwell, 69 kN/m² |
| 3 . | RH: 0 to 5% |
| 4 . | 38°C, 90%RH |
| 5 . | 2.5° wide angle |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9860 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Bergamid™ A70 G20 H BK014 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Arnitel® PL650 | DSM Engineering Plastics | TPC-ET | Arnitel® |
| ENGAGE™ 8100 | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| LEXAN™ LUX9616 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |