Boda BDP-H7701

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	Chenguang Fluoro & Silicone Elastomers Co., Ltd.
Trademark:	Boda
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	NF5z13_Boda-BDP-H7701.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Material Type: Black color fluoroelastomer compound, hardness Shore A 65~75.
Based on peroxide curable fluoroelastomer with high fluorine content.

Features:

Short post cure time

Excellent mold flow and mold release, resulting in less flash

Improved bonding property to metal.

Good at coolant resistance.

Extraordinary chemical resistance:

Alcohol Fuel

Steam

Acids

Chemicals containing amines

Process Methods: Suitable for compression, transfer, injection and extrusion molding processes.

Applications: injection molding of cylinder head gaskets, O-rings and other complicated geometries.

Lab Testing Curing Condition:

Press Curing: 10min@170°C.

Oven: (1+4)hrs@230°C

General Information
Features	Acid Resistant Alcohol Resistant Bondability Fuel Resistant Good Flow Good Mold Release Good Moldability Minimal Flash Steam Resistant
Uses	Gaskets
Appearance	Black
Processing Method	Compression Molding Extrusion Injection Molding Resin Transfer Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.98	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	73		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	17.3	MPa	ASTM D412
Tensile Elongation (Break)	290	%	ASTM D412
Compression Set ¹(200°C, 70 hr)	20	%	ASTM D395

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air (250°C, 70 hr)	-9.0	%	ASTM D573
Change in Ultimate Elongation in Air (250°C, 70 hr)	-13	%	ASTM D573
Change in Durometer Hardness in Air (250°C, 70 hr)	2.0		ASTM D573
Change in Tensile Strength (23°C, 70 hr, in Reference Fuel C)	-4.0	%	ASTM D471
Change in Ultimate Elongation (23°C, 70 hr, in Reference Fuel C)	-9.0	%	ASTM D471
Change in Durometer Hardness (23°C, 70 hr, in Reference Fuel C)	-2.0		ASTM D471
Change in Volume (23°C, 70 hr, in Reference Fuel C)	2.0	%	ASTM D471

Note Message
1 .	6 mm Buttons

Resin Grade	Manufacturer	Category	Trademark
RTP 201 D	RTP Company	Nylon 612	RTP
Prime Polypro™ J227T	Prime Polymer Co., Ltd.	PP Random Copolymer	Prime Polypro™
Grivory® GV-5H black	EMS-GRIVORY	Nylon 66+Nylon 6I/X	Grivory®
Polifor® 1 BS/25 NATURALE	SO.F.TER. SPA	PP Homopolymer	Polifor®
ExxonMobil™ HDPE HTA 002HD5	ExxonMobil Chemical	HDPE, UHMW	ExxonMobil™ HDPE