Alathon® L4903
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NEvGzi_Alathon-L4903.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Alathon L4903 is a high molecular weight high density copolymer with broad bimodal molecular weight distribution. This resin exhibits excellent machine direction tear in an HMW-HD resin as well as low gel levels. Typical applications include trash can liners and products requiring incorporation of PCR. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.027 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 13 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 13 µm | 993 | MPa | ASTM D882 |
| TD : 13 µm | 1020 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 13 µm | 37.2 | MPa | ASTM D882 |
| TD : Yield, 13 µm | 28.3 | MPa | ASTM D882 |
| MD : Broken, 13 µm | 80.0 | MPa | ASTM D882 |
| TD : Broken, 13 µm | 52.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 13 µm | 330 | % | ASTM D882 |
| TD : Broken, 13 µm | 410 | % | ASTM D882 |
| Dart Drop Impact 1(13 µm) | 230 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 13 µm | 10 | g | ASTM D1922 |
| TD : 13 µm | 60 | g | ASTM D1922 |
| Extrusion instructions |
|---|
| Film Data Obtained Under the Following Extrusion Conditions:Alpine 200 mm 3 Layer Die (40/35/25); 3 Extruders: 65 mm / 75 mm / 50 mm; Die Gap = 1.5 mm; Film Thickness = 0.5 mil; 500 lbs/ hr; Internal Bubble Cooling; Neck Height = 8 x DD; Blow Up Ratio = 4:1 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP6850 B38 | Spartech Polycom | PP, Unspecified | Spartech |
| TRANSMARE® 22CT25-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Clariant Nylon 6 PA213G33 | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| Edgetek™ AS/018 White | PolyOne Corporation | ABS | Edgetek™ |
| TAFMER™ XM-5070S | Mitsui Chemicals, Inc. | PAO | TAFMER™ |