Kelon® A H CEG/40
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Kelon® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NEuBhL_Kelon-A-H-CEG-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 66 (PA 66). Heat stabilised. Mineral filler / Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.0 to 1.3 | % | |
| Flow : 2.00 mm | 0.80 to 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 6600 | MPa | |
| 60°C | 5000 | MPa | |
| 90°C | 4100 | MPa | |
| 120°C | 3700 | MPa | |
| 150°C | 2600 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 90.0 | MPa | |
| Break, 60°C | 70.0 | MPa | |
| Break, 90°C | 45.0 | MPa | |
| Break, 120°C | 35.0 | MPa | |
| Break, 150°C | 25.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.9 | % | |
| Break, 60°C | 3.5 | % | |
| Break, 90°C | 7.0 | % | |
| Break, 120°C | 8.0 | % | |
| Break, 150°C | 12 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 35 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 125 | °C | |
| Vicat Softening Temperature | 230 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 203 H | RTP Company | Nylon 66 | RTP |
| Flontech® FT-STST50-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Gallonprene® GP520-7005 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Halene L 73005T | Haldia Petrochemicals Ltd. | LLDPE | Halene L |
| Jiangsu Sinarise ZM828 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |