DOWLEX™ 2601
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NEGTSg_DOWLEX-2601.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
DOWLEX™ Polyethylene Resin is designed for the production of a wide variety of film applications. Films made from this resin exhibit a combination of good toughness and tear resistance.
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.924 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 4.88 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 180 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 218 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 11.9 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 12.4 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 40.7 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 32.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 680 | % | ASTM D882 |
| TD : Fracture, 51 µm | 730 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 170 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 680 | g | ASTM D1922 |
| TD : 51 µm | 1100 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 108 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 122 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 59 | ASTM D2457 | |
| Haze (50.8 µm) | 13 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm) 30:1 L/D 螺杆类型：DSBII 模具间隙：70 密尔 (1.8 mm) 输出：模具周长的 10 磅/小时/英寸 模具直径：6 英寸 放大比：2.5 : 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1400 AG-320 | RTP Company | PESU | RTP |
| XYRON™ AG512 | Asahi Kasei Chemicals Corporation | Nylon+PPE | XYRON™ |
| Flontech® FT-CAR33-GR2-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Hostaform® C 9021 GV3/20 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| MAJORIS G409/12.5 - 8229 | AD majoris | PP, Unspecified | MAJORIS |