Genestar™ GW1458HF
| Category: | Nylon 9T , Polyamide 9T |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | Genestar™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NE08Fc_Genestar-GW1458HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The G1300H and G1350H are suitable for use in a wide range of electrical and electronics components as UL94 HB flammability rating, while the G1302 grade delivers low friction. HB grades do not contain halogen-containing flame-retardants. The GW1458HF offers low warpage and high flow-ability. *'Halogen free' follows the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (320°C/2.16 kg) | 90 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 1.00 mm | 0.050 | % | |
| Across Flow : 1.00 mm | 0.50 | % | |
| Water Absorption 1(Equilibrium, 40°C, 95%RH) | 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 150 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.1 | % | ASTM D638 |
| Flexural Modulus | 13000 | MPa | ASTM D790 |
| Flexural Strength | 207 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 290 | °C | ASTM D648 |
| Glass Transition Temperature | 125 | °C | |
| Melting Temperature | 306 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 2(320°C, 500.0 µm) | 6.20 | cm | |
| Weld Elongation | 0.40 | % | ASTM D638 |
| Weld Strength | 32.0 | MPa | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | 96 hrs |
| 2 . | 750kgf |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-6355B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| ACCUTECH™ HP0334M30CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| BMC 840-6558 | Bulk Molding Compounds, Inc. | Vinyl Ester | BMC |
| HiFill® PP GB40 | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| MAJORIS EW305 - 7818 | AD majoris | PP, Unspecified | MAJORIS |