Plyophen 23057

Category:	Phenolic , Phenolic
Manufacturer:	Durez Corporation
Trademark:	Plyophen
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	NDuDkl_Plyophen-23057.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Plyophen 23057 is a liquid one-step phenolic resin in ethanol. Plyophen 23057 is a polyamide modified phenolic resin which was developed especially for use with glass cloth to produce laminates which will have an increased degree of burn-through resistance, and is suggested for those applications requiring improved physical properties on short exposure to temperatures above 600°F. The data given below is based on the use of glass cloth impregnated with this resin. However, certain modifications can be incorporated, such as the use of certain fillers, which may prove beneficial in certain cases. Fillers such as aluminum phosphate, graphite and others, may be incorporated with the resin in amounts up to 10% or more and in some cases beneficial results will be obtained, especially when the temperature of exposure goes to a fairly high temperature where some of the fillers may become reactive with the glass.

Message

Plyophen 23057 is a liquid one-step phenolic resin in ethanol.

Plyophen 23057 is a polyamide modified phenolic resin which was developed especially for use with
glass cloth to produce laminates which will have an increased degree of burn-through resistance, and is suggested for those applications requiring improved physical properties on short exposure to
temperatures above 600°F.

The data given below is based on the use of glass cloth impregnated with this resin. However, certain
modifications can be incorporated, such as the use of certain fillers, which may prove beneficial in certain cases. Fillers such as aluminum phosphate, graphite and others, may be incorporated with the resin in amounts up to 10% or more and in some cases beneficial results will be obtained, especially when the temperature of exposure goes to a fairly high temperature where some of the fillers may become reactive with the glass.

General Information
Features	High Heat Resistance
Uses	Coating Applications Laminates

Thermoset	Nominal Value	Unit	Test Method
Thermoset Mix Viscosity (25°C)	1500	cP	Internal Method
Post Cure Time (275°C)	18	hr

Additional Information	Nominal Value	Unit	Test Method
Non-Volatile Content	43	%	Internal Method
Sunshine Gel (135°C)	23.0	min	Internal Method

Resin Grade	Manufacturer	Category	Trademark
RTP 182 HEC	RTP Company	PP, Unspecified	RTP
RTP 1399 X 106389	RTP Company	PPS	RTP
Complet® LGF50-PA66	PlastiComp, Inc.	Nylon 66	Complet®
Hifax CB252	LyondellBasell Industries	TPO (POE)	Hifax
Petrothene® LT543501	LyondellBasell Industries	HDPE	Petrothene®