RTP 300.5 Z
| Category: | PC , Polycarbonate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NBnwbE_RTP-300-5-Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.14 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength | 65.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength | 96.5 | MPa | ASTM D790 |
| Compressive Strength | 89.6 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 130 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1900 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 141 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 135 | °C | ASTM D648 |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.010 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-1 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 6mil/in.Tensile Elongation, ASTM D-638: 10-20% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 288 - 343 | °C | |
| Middle Temperature | 288 - 343 | °C | |
| Front Temperature | 288 - 343 | °C | |
| Mold Temperature | 65.6 - 121 | °C | |
| Injection Pressure | 103 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLUX® (MABS) Typ C12 | A. Schulman Europe | MABS | POLYLUX® |
| Sanren Y3500 (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| AKROMID® A3 GF 60 1 natural (2396) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| EMOPLEN® A 1025 T15 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| Globalprene® 3412P | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |