Arlon® 1330
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Greene, Tweed & Co. |
| Trademark: | Arlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NB8gx5_Arlon-1330.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Greene, Tweed offers precision plastic components for a variety of demanding, semiconductor applications. These components are made from a full range of high-performance plastic materials including Arlon® 1330. Ideal for applications requiring exceptional wear resistance and chemical compatibility, Arlon 1330 provides good dimensional stability without the addition of carbon fibers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.35 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 86.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 20 | % | ASTM D638 |
| Flexural Modulus - 0.5% Secant | 3690 | MPa | ASTM D790 |
| Flexural Strength | 145 | MPa | ASTM D790 |
| Compressive Strength 1 | 107 | MPa | ASTM D695 |
| Shear Strength 2 | ASTM D732 | ||
| 23°C | 77.6 | MPa | |
| 232°C | 19.8 | MPa | |
| Coefficient of Friction 3 | 0.15 | ASTM D1894 | |
| Wear Factor | 40 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 57 | J/m | ASTM D256 |
| Unnotched Izod Impact | 1000 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 166 | °C | ASTM D648 |
| Melting Temperature | 343 | °C | |
| CLTE - Flow | ASTM D696 | ||
| < 149°C | 4.1E-5 | cm/cm/°C | |
| > 149°C | 1.5E-4 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Break |
| 2 . | Axial |
| 3 . | PV=12,600 psi ft/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viprene™ P40D-22U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| Anjatech® 250-E/H/GF30 | Almaak International GmbH | Nylon 6 | Anjatech® |
| Exxtral™ Performance Polyolefin LNT010 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Genestar™ GA2330 | Kuraray Co., Ltd. | Nylon 9T | Genestar™ |
| OP - PC/PBT 802-I | Oxford Polymers | PC+PBT | OP - PC/PBT |