CAPRAN MEDALLION® films from Honeywell are biaxially oriented nylon 6 films with excellent strength and barrier properties. They are well suited for a variety of packaging applications.

General Information
Features	High strength Perforation resistance Good cracking resistance Definition, high Good toughness Barrier resin
Uses	Films Laminate Food packaging
Forms	Films

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D955
Flow : 0.0152mm	1.5 - 2.5	%	ASTM D955
Transverse flow : 0.0152mm	1.0 - 2.0	%	ASTM D955

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With Metal-Dynamic	0.19	ASTM D1894
With self-dynamics	0.50	ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	15	µm
secant modulus			ASTM D882
MD : 15 µm	3100	MPa	ASTM D882
TD : 15 µm	2550	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Break, 15 µm	276	MPa	ASTM D882
TD : Break, 15 µm	345	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Break, 15 µm	100	%	ASTM D882
TD : Break, 15 µm	75	%	ASTM D882
Oxygen Permeability (25°C, 15 µm)	1.6	cm³·mm/m²/atm/24 hr	ASTM D3985
Water Vapor Transmission Rate (15 µm, 38°C, 100% RH)	330	g·mm/m²/atm/24 hr	ASTM F1249

Optical	Nominal Value	Unit	Test Method
Gloss (20°, 15.2 µm)	130 - 150		ASTM D2457
Haze (15.2 µm)	2.0 - 3.0	%	ASTM D1003

Additional Information
Yield: 40044 in²/lbTensile Strength @ Break, ASTM D 882, MD: 35000 to 45000 psiTensile Strength @ Break, ASTM D 882, TD: 45000 to 55000 psiElongation @ Break, ASTM 882, MD: 90 to 110%Elongation @ Break, ASTM 882, TD: 65 to 85%Secant Modulus, ASTM D 882, MD: 400000 to 500000 psiSecant Modulus, ASTM D 882, TD: 320000 to 420000 psiGraves Tear (initial), ASTM D 1004, MD: 1000 to1400 g/milGraves Tear (initial), ASTM D 1004, TD: 1100 to1500 g/milCoefficient of Friction, ASTM D 1894: 0.40 to 0.60 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.13 to 0.24 vs Metal-DynamicSurface Tension, ASTM D5946, treated side: >/= 56 dynes/cmSurface Tension, ASTM D5946, untreated side: >50 dynes/cmWater Vapor Transmission ASTM F 1249, 100°F, 100%RH: 20 to 23 g/100 in²/dayOxygen Transmission Rate, ASTM D3985, 77°F, 0%RH: 3.0 to 4.0 cc/100in²/day

Additional Information

Yield: 40044 in²/lbTensile Strength @ Break, ASTM D 882, MD: 35000 to 45000 psiTensile Strength @ Break, ASTM D 882, TD: 45000 to 55000 psiElongation @ Break, ASTM 882, MD: 90 to 110%Elongation @ Break, ASTM 882, TD: 65 to 85%Secant Modulus, ASTM D 882, MD: 400000 to 500000 psiSecant Modulus, ASTM D 882, TD: 320000 to 420000 psiGraves Tear (initial), ASTM D 1004, MD: 1000 to1400 g/milGraves Tear (initial), ASTM D 1004, TD: 1100 to1500 g/milCoefficient of Friction, ASTM D 1894: 0.40 to 0.60 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.13 to 0.24 vs Metal-DynamicSurface Tension, ASTM D5946, treated side: >/= 56 dynes/cmSurface Tension, ASTM D5946, untreated side: >50 dynes/cmWater Vapor Transmission ASTM F 1249, 100°F, 100%RH: 20 to 23 g/100 in²/dayOxygen Transmission Rate, ASTM D3985, 77°F, 0%RH: 3.0 to 4.0 cc/100in²/day

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Honeywell
Trademark:	Capran Medallion®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	NAPSzI_Capran-Medallion-1500-film.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Vinnolit® EP 7091	Vinnolit GmbH & Co. KG	PVC Homopolymer	Vinnolit®
Next Nylon 66 Prime Series PGF30-01NC	Next Polymers Ltd.	Nylon 66	Next Nylon 66 Prime Series
ACLAR® 33C	Honeywell	PCTFE	ACLAR®
Geon™ BIO RB9000	PolyOne Corporation	PVC, Flexible	Geon™ BIO
Sylvin 8240-80FU Brown 7425	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin