NORYL™ GFN2F resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NAPLVV_NORYLGFN2Fresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPE+PS blend. 20% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump housings and impellers, valve components and others. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 12 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 2.40 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.20 - 0.40 | % | Internal method |
| Water Absorption | |||
| 24 hr | 0.060 | % | ASTM D570 |
| 23°C, 24 hr | 0.12 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6500 | MPa | ASTM D638 |
| -- | 6000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 100 | MPa | ASTM D638 |
| Yield 3 | 88.0 | MPa | Internal method |
| Yield | 90.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 6.0 - 8.0 | % | Internal method |
| Fracture 5 | 3.0 | % | ASTM D638 |
| Fracture | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 100mm span 6 | 5570 | MPa | ASTM D790 |
| -- 7 | 5400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 150 | MPa | ISO 178 |
| Yield, 100mm span 8 | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 88 | J/m | ASTM D256 |
| -30°C 10 | 9.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 550 | J/m | ASTM D4812 |
| 23°C 12 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 20.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 137 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 138 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 13 | 135 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/B50 |
| -- | 147 | °C | ISO 306/B120 |
| CLTE - Flow (-30 to 30°C) | 2.8E-5 - 4.5E-5 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 266 - 316 | °C | |
| Middle Temperature | 277 - 321 | °C | |
| Front Temperature | 288 - 327 | °C | |
| Nozzle Temperature | 299 - 327 | °C | |
| Processing (Melt) Temp | 299 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 10mm/min |
| 4 . | Type 1, 10mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 2.6 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.6 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Andur 1-8 APLM/Curene® 442 | Anderson Development Company | PUR-Ester/TDI | Andur |
| Flontech® FT-GL15-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Geon™ Vinyl Rigid Molding M4605 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| LNP™ STAT-KON™ DEP23FXC compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| POLYabs S00 AS UV | Polykemi AB | ABS | POLYabs |