LNP™ THERMOCOMP™ DF002H compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NALzal_LNP-THERMOCOMP-DF002H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* DF002H is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added feature includes: Healthcare. Also known as: LNP* THERMOCOMP* Compound DF-1002 HC Product reorder name: DF002H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 to 0.60 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.14 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4250 | MPa | ASTM D638 |
| -- | 4170 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 81.0 | MPa | ASTM D638 |
| Yield | 80.0 | MPa | ISO 527-2/5 |
| Break 3 | 75.0 | MPa | ASTM D638 |
| Break | 74.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.9 | % | ASTM D638 |
| Yield | 3.8 | % | ISO 527-2/5 |
| Break 5 | 5.6 | % | ASTM D638 |
| Break | 5.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 4110 | MPa | ASTM D790 |
| -- 7 | 3960 | MPa | ISO 178 |
| Flexural Strength 8(Yield, 50.0 mm Span) | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 81 | J/m | ASTM D256 |
| 23°C 9 | 8.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 880 | J/m | ASTM D4812 |
| 23°C 10 | 55 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 18.4 | J | ASTM D3763 |
| -- | 10.5 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 146 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 141 | °C | |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1385 UP | RTP Company | PPS | RTP |
| RTP 283E | RTP Company | Nylon, Unspecified | RTP |
| Trexlink™ 6770 GM | Mitsubishi Chemical Performance Polymers, Inc. | TPE | Trexlink™ |
| DIOSHY® TPU T980M | DIOSHY Co.,Ltd. | TPU-Polyester | DIOSHY® |
| Guang Sung PVC GPMD80 | Guang Sung Plastics (GSPL) | PVC, Rigid | Guang Sung PVC |