Alloy Exchange Reprocessed PC001
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Alloy Exchange, Inc. |
| Trademark: | Alloy Exchange Reprocessed |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NAARIS_Alloy-Exchange-Reprocessed-PC001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Alloy Exchange Reprocessed PC001 is a Polycarbonate + ABS (PC+ABS) material. It is available in North America. Primary attribute of Alloy Exchange Reprocessed PC001: Eco-Friendly/Green. |
| General Information | |
|---|---|
| Recycled Content |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.12 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.9 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (3.29 mm) | 47.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.29 mm) | 20 | % | ASTM D638 |
| Flexural Modulus - Tangent (3.28 mm, 50.0 mm Span) | 2280 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(3.22 mm) | 500 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 3(1.8 MPa, Unannealed) | 98.0 | °C | ASTM D648A |
| Note Message | |
|---|---|
| 1 . | No. of specimens tested: 3 |
| 2 . | No. of specimens tested: 5 |
| 3 . | No. of specimens tested: 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1403 N | RTP Company | PESU | RTP |
| Sarlink® TPE ML-1140DB BLK X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| ARMAMID® PA HC 20-1AF | Poly Plastic | Nylon 6 | ARMAMID® |
| Cheng Yu SW15 | Cheng Yu Plastic Company Limited | Acetal (POM) Copolymer | Cheng Yu |
| Kepital® FM2020 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |