Prisma® 2400
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Braskem |
| Trademark: | Prisma® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N8bUX8_Prisma-2400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: Prisma 2400 is a high melt flow rate random copolymer. This product is design for ISBM process (Injection Stretch Blow Molding) and offers low taste/odor. Applications: Injection of transparent parts for packages; ISBM technology transparent bottles for mineral water, teas, cold juices, drinks and isotonic beverages. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.902 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, Injection Molded | 71 | ASTM D785 | |
| R-Scale | 71 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 28.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 16 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 1% Secant : Injection Molded | 950 | MPa | ASTM D790 |
| Injection Molded | 1000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -20°C, Injection Molded | 15 | J/m | ASTM D256 |
| 23°C, Injection Molded | 40 | J/m | ASTM D256 |
| -20°C, Injection Molded | 1.3 | kJ/m² | ISO 180 |
| 23°C, Injection Molded | 2.2 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 74.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 74.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 47.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 47.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 127 | °C | ISO 306/A, ASTM D1525 1 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | |||
| 1000 µm, Injection Molded | 12 | % | ASTM D1003 |
| 1000 µm, Injection Molded | 12 | % | ISO 13468-1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SARANEX™ 450 | The Dow Chemical Company | PVDC | SARANEX™ |
| SCHULAMID® 66 GF 30 FR 4 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Selvol™ WS-53NF | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| LOXIM 230 12 HB | LOXIM Industries Private Limited | PBT | LOXIM |
| PENTAMID B L5 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |