GLAMIDE® T-714E
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N8PYYg_GLAMIDE-T-714E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GLAMIDE®T-714E is a polyamide product,. It is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.18 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.10 - 0.30 | -- | % | ASTM D955 |
| 3.00 mm | 0.40 - 0.70 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.3 | -- | % | ASTM D570 |
| Equilibrium, 65% RH | 2.4 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 130 | 125 | MPa | ASTM D638 |
| Yield, 23°C | 97.0 | 92.0 | MPa | ASTM D638 |
| Yield, 80°C | 80.0 | 16.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 50 | 50 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 3800 | 3500 | MPa | ASTM D790 |
| 23°C | 2600 | 2500 | MPa | ASTM D790 |
| 80°C | 2000 | 500 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 195 | 185 | MPa | ASTM D790 |
| Yield, 23°C | 147 | 135 | MPa | ASTM D790 |
| Yield, 80°C | 121 | 25.0 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 100 | -- | MPa | ASTM D695 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 20 | 20 | J/m | ASTM D256 |
| 23°C | 60 | 60 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 100 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 118 | -- | °C | ASTM D648 |
| CLTE - Flow | 5.4E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 19 | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 4.00 | 4.00 | ASTM D150 | |
| Arc Resistance | 110 | 110 | sec | ASTM D495 |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Comparative Tracking Index, IEC Method: >600 V |
| 调节后的 Comparative Tracking Index, IEC Method: >600 V |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Pressure | 40.0 - 50.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2582 HEC FR | RTP Company | PC+ABS | RTP |
| RELENE® 52GB001 | Reliance Industries Limited | HDPE, HMW | RELENE® |
| Stylac™ 789 | Asahi Kasei Chemicals Corporation | AS | Stylac™ |
| Vipel® F010-CNP-25 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| INNOPOL® PP CS 1-5140 LH | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |