STYRON A-TECH™ 1400-AS
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Americas Styrenics LLC |
| Trademark: | STYRON A-TECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N7pQL6_STYRON-A-TECH-1400-AS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STYRON A- TECH™1400-AS is a high impact polystyrene material,. This product is available in North America and is processed by injection molding. STYRON A- TECH™The main features of 1400-AS are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 9.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 103 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 1700 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Fracture, injection molding | 21.0 | MPa | ASTM D638 |
| Injection Molding | 22.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Injection Molded) | 70 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 1700 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 31.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, molded | 85 | J/m | ASTM D256 |
| 23°C, injection molding | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 88.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 78.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 218 - 249 | °C | |
| Middle Temperature | 218 - 249 | °C | |
| Front Temperature | 199 - 213 | °C | |
| Nozzle Temperature | 213 - 243 | °C | |
| Mold Temperature | 15.6 - 65.6 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.200 - 1.20 | MPa | |
| Cushion | 6.35 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 177 - 193 | °C | |
| Cylinder Zone 2 Temp. | 182 - 204 | °C | |
| Cylinder Zone 3 Temp. | 188 - 210 | °C | |
| Cylinder Zone 4 Temp. | 199 - 216 | °C | |
| Cylinder Zone 5 Temp. | 204 - 221 | °C | |
| Adapter Temperature | 193 - 232 | °C | |
| Melt Temperature | 193 - 232 | °C | |
| Die Temperature | 199 - 232 | °C |
| Extrusion instructions |
|---|
| Zone 6 Temperature: 204 to 221°CMelt Pump, Pipes, Screen Changer Temperature: 193 to 232°CPolish Rolls Temperature: 66 to 104°CHead Pressure: 10 to 21 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 226 | SAX Polymers | Nylon 66 | SAXAMID™ |
| Wellamid® GF1398 BK12 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Elastron® V V201.A65.B | Elastron USA, Inc. | TPV | Elastron® V |
| Electrafil® J-80/CF/20 NAT | Techmer Engineered Solutions | Acetal (POM) Copolymer | Electrafil® |
| LNP™ STAT-KON™ DE002 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |