LNP™ LUBRICOMP™ DP003EH compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N7QevE_LNP-LUBRICOMP-DP003EH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DP003EH is a compound based on Polycarbonate resin containing 15% PTFE/Silicone. Added features of this material include: Easy Molding, Wear Resistant, Healthcare. Also known as: LNP* LUBRICOMP* Compound DL-4530 EM HC Product reorder name: DP003EH |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 to 0.90 | % | |
| Across Flow : 24 hr | 0.70 to 1.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.13 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.19 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2030 | MPa | ASTM D638 |
| -- | 2010 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 40.7 | MPa | ASTM D638 |
| Yield 2 | 49.0 | MPa | ASTM D638 |
| Yield | 48.0 | MPa | ISO 527-2/5 |
| Break | 46.2 | MPa | ASTM D638 |
| Break 3 | 43.0 | MPa | ASTM D638 |
| Break | 46.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield | 5.0 | % | ASTM D638 |
| Yield 4 | 5.9 | % | ASTM D638 |
| Yield | 5.7 | % | ISO 527-2/5 |
| Break | 17 | % | ASTM D638 |
| Break 5 | 49 | % | ASTM D638 |
| Break | 120 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- | 2060 | MPa | ASTM D790 |
| 50.0 mm Span 6 | 2100 | MPa | ASTM D790 |
| -- 7 | 1930 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 77.9 | MPa | ASTM D790 |
| -- | 61.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.29 | ||
| vs. Itself - Static | 0.16 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | -0.300 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 28.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 470 | J/m | ASTM D256 |
| 23°C 8 | 41 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1500 | J/m | ASTM D4812 |
| 23°C 9 | 170 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 29.7 | J | ASTM D3763 |
| -- | 20.5 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 140 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 128 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 127 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 7.8E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 6 B11^ FX25 FR10 | Polykemi AB | Nylon 6 | SCANAMID 6 |
| TECHNYL® A 218W V33 NATURAL T | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Comai 407-1 NT | Comai Ltda | PP Homopolymer | Comai |
| KEBAFLEX® U A 75 ST B01 natural | BARLOG plastics GmbH | TPU, Unspecified | KEBAFLEX® |
| LNP™ THERMOCOMP™ JF004EXP compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |