TechnoDur PBT/PET GF 20 Natural (9969)
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | TechnoCompound GmbH |
| Trademark: | TechnoDur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N6wW3k_TechnoDurPBTPETGF20Natural9969.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TechnoDur: Braves extremely low Temperatures Our new TechnoDur PBT compound is a thermoplastic which combines great hardness, stiffness and strength. TechnoDur is easily processed due to its perfect flow behaviour. The favourable sliding and wear characteristics as well as extremely high tenacity in temperatures below freezing are further advantages. Typical Applications TechnoDur compounds may be applied in the following areas:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (265°C/2.16 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Transverse flow | 1.0 | % | ISO 2577 |
| Flow | 0.30 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.20 | % | ISO 62 |
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness 2 | 200 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 135 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 3 | 6200 | MPa | ISO 178 |
| Flexural Stress 4 | ISO 178 | ||
| -- | 195 | MPa | ISO 178 |
| 3.5% strain | 195 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 5 | 3.5 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 95.0 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| Melting Temperature 6 | 220 - 255 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 26 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.80 | IEC 60250 | |
| 1 MHz | 3.60 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | HB | Internal method | |
| Glow Wire Flammability Index (2.0 mm) | 750 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 260°C / WZ 80°C, 600 bar |
| 2 . | 358 N |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 HT 7500 GF 50 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Vipel® K190-RTM-17 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Nipol® NBR DN3335 | Zeon Corporation | NBR | Nipol® NBR |
| Globalprene® 9551U | Lee Chang Yung Chemical Industry Corp. | SEBS | Globalprene® |
| Petrothene® NA204000 (Extrusion Coating) | LyondellBasell Industries | LDPE | Petrothene® |