AVP™ KLL20CP
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | AVP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N6nkuX_AVP-KLL20CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AVP™ KLL20CP is a Polycarbonate (PC) product filled with 20% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.18 mm) | 72.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.18 mm) | 7.0 | % | ASTM D638 |
| Flexural Modulus 3(3.18 mm) | 5170 | MPa | ASTM D790 |
| Flexural Strength 4(3.18 mm) | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 143 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, BLK) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Rear Temperature | 288 to 299 | °C | |
| Middle Temperature | 294 to 321 | °C | |
| Front Temperature | 294 to 321 | °C | |
| Nozzle Temperature | 294 to 321 | °C | |
| Processing (Melt) Temp | 310 to 338 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 1.38 | MPa |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ OLS100 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| Sumitomo Silicone SI 9045C | Sumitomo Bakelite North America, Inc. | Silicone | Sumitomo Silicone |
| TRIREX® 3030U | Samyang Corporation | PC | TRIREX® |
| AVALON® 60 ABX | Huntsman Corporation | TPU-Polyester | AVALON® |
| Karina BLACK PVC COMPOUND 751-48/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |