Baypreg® F 315 (10 mm Glass Mat Reinforced Sandwich)
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baypreg® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N6R9US_Baypreg-F-315-10-mm-Glass-Mat-Reinforced-Sandwich-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baypreg F 315 system is a two component polyurethane system used in compression molding of fiber-reinforced sandwich panels to produce a variety of automotive parts. Some identified applications include door panels, sunshades, spare tire covers, load floors, etc. The Baypreg F 315 system provides lightweight alternatives to ABS, PP, SMC, and wood products while demonstrating very high flexural stiffness and excellent thermal properties. Baypreg F 315 system offers very diverse properties over a wide range of part thicknesses and densities while still providing cost effective substrate parts when combined with reinforcing materials. As with any product, use of the Baypreg F 315 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.189 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (22°C) | 2900 | MPa | ASTM D790 |
| Flexural Strength (22°C) | 8.00 | MPa | ASTM D790 |
| Thermoset | Nominal Value | ||
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 190 | ||
| Component B | Mixing ratio by weight: 100 |
| Additional Information |
|---|
| Part A Type: Isocyanate Appearance: Dark Brown Liquid Specific Gravity @ 25°C: 1.21 Viscosity @25°C: 350 mPa Flash Point, PMCC: 223°C NCO: 28.5 wt% Part B Type: Polyol Appearance: Black liquid Specific Gravity @ 25°C: 1.10 Viscosity @25°C: 2700 mPa-s Flash Point, PMCC: 170°C Hydroxyl Number: 685 KOH/g Reinforcing Mat Weight: 600 g/m³Molded Thickness: 10 mmChemical Temperature: 21 to 27°CMold Temperature: 100 to 120°CCure Time: 65 to 95 secTime from Spray to Close: 70 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Milastomer™ 8032NS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| Spartech Polycom 1144-4-62 | Spartech Polycom | PVC Alloy | Spartech |
| Vydyne® R550H NT453 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| PermaStat® 1200 T-70A | RTP Company | TPU-Polyether | PermaStat® |
| POLYMAN® FSAN GF 35 K2405 | A. Schulman Europe | SAN | POLYMAN® |