Moplen 2000HEXP
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N5rMSh_Moplen-2000HEXP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen 2000HEXP is a medium fluidity heterophasic copolymer development grade with an additivation suitable for injection moulding applications. It exhibits an outstanding impact performance, particularly at low temperature combined with a good processability. The resin is particularly designed for injection moulding applications where very high impact performance is critical. "Moplen" 2000HEXP can be used in luggage, closures and as an ideal base material for technical compounding. It is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 22.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 43.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 19.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | |
| Break | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 6.5 | kJ/m² | |
| 0°C | 8.0 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength (-20°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 76.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/A50 |
| -- | 55.0 | °C | ISO 306/B50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| FHR Polypropylene AP5106-HA | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Hostalen PP EBG 252D | LyondellBasell Industries | PP Impact Copolymer | Hostalen |
| LUVOCOM® 1850-8282 | Lehmann & Voss & Co. | PBT | LUVOCOM® |
| Axiall PVC 3265 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Durethan® BM 25 FN20 DUS013 000000 | LANXESS GmbH | Nylon 6 | Durethan® |