ASTALAC™ ABS MGP22
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N2M3NI_ASTALAC-ABS-MGP22.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALAC™ ABS MGP22 is a high melt flow and high impact strength grade of ABS which is designed for injection moulding applications requiring excellent toughness and abuse resistance whilst maintaining a balance of product rigidity, heat resistance and mouldability. Typical applications include automotive grilles and appliques, telecommunications housings and appliance cases. Note: The letters "UV" included as a suffix indicates UV stabilisation has been added [ ie: ASTALAC™ ABS MGP22UV ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 24 | g/10 min | |
| 230°C/3.8 kg | 6.0 | g/10 min | |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 39.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 40 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2050 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 63.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 300 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 40.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 75.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 80.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 87.0 | °C | |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 5 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 205 to 225 | °C | |
| Middle Temperature | 215 to 235 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC8FRN (Series: FR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Tritan™ MX711 | Eastman Chemical Company | Copolyester | Tritan™ |
| PENTAMID B GV40 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| Plexiglas® Diffuse V045-68194 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| Sylvin 83043-75FUV Yellow 4162 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |