Ultraform® N 2770 K
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultraform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N1gNlp_Ultraform-N-2770-K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection molding grade with enhanced wear behavior for sliding parts. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Apparent Density | 0.85 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 7.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 2.1 | % | ISO 294-4 |
| Flow direction | 2.1 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.80 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 140 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 8.5 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 26 | % | ISO 527-2/50 |
| Tensile Creep Modulus 1(1000 hr) | 1400 | MPa | ISO 899-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.5 | kJ/m² | ISO 179/1eA |
| 23°C | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 150 | kJ/m² | ISO 179/1eU |
| 23°C | 150 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 95.0 | °C | ISO 75-2/A |
| Melting Temperature | 166 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 55°C) | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Maximum operating temperature- short cycle operation | 100 | °C |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Passed | FMVSS 302 | |
| ISO Type | POM-K, M-GNRS2, 03-002 | ISO 9988-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 85 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.80 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 5.0E-3 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Hopper Temperature | 200 | °C | |
| Rear Temperature | 200 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 200 | °C | |
| Nozzle Temperature | 200 | °C | |
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 60.0 - 120 | °C |
| Injection instructions |
|---|
| Residence Time : <10 min |
| Note Message | |
|---|---|
| 1 . | strain <= 0,5%, 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V914 BLK580 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sindustris ABS LSG286NS | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| TOTAL Polyethylene D3720 | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| Ferro PP TPP20AE54WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| Ecomass® 1080ZD93 | Ecomass Technologies | Nylon, Unspecified | Ecomass® |