Plaslube® HIPS E SL5
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N09qEi_Plaslube-HIPS-E-SL5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube® HIPS E SL5 is a High Impact Polystyrene product. It can be processed by extrusion and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/1.2 kg | 2.0 | g/10 min | |
| 230°C/3.8 kg | 33 | g/10 min | |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 60 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 26.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 44 | % | ASTM D638 |
| Flexural Modulus | 1450 | MPa | ASTM D790 |
| Flexural Strength | 34.5 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.060 | ||
| vs. Steel - Static | 0.080 | ||
| Wear Factor | 60 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 96.1 | °C | |
| 1.8 MPa, Unannealed | 85.0 | °C | |
| CLTE - Flow | 6.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 302 SE | RTP Company | PC | RTP |
| WPP TPO TPO-257 | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| Plenco 01508 (Injection) | Plastics Engineering Co. | Polyester, TS | Plenco |
| POFEX 8200EP80M | POLYROCKS CHEMICAL CO., LTD | TPE | POFEX |
| POLIMAXX KU650 | IRPC Public Company Limited | ABS | POLIMAXX |