PALRAN® R S H 08 GF 16

Category:	ABS , Acrylonitrile Butadiene Styrene
Manufacturer:	pal plast GmbH
Trademark:	PALRAN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	MzgB0B_PALRAN-R-S-H-08-GF-16.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PALRAN®R S H 08 GF 16 is an acrylonitrile butadiene styrene (ABS) product, which contains a filler of 16% glass fiber reinforcement. It can be processed by injection molding and is available in Europe. PALRAN®The application fields of R S H 08 GF 16 include electrical appliances and automotive industries. Features include: flame retardant/rated flame High stiffness Heat resistance

General Information
Filler / Reinforcement	Glass fiber reinforced material, 16% filler by weight
Features	Rigidity, high Heat resistance, high
Uses	Electrical appliances Application in Automobile Field
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.16	g/cm³	ISO 1183

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	5250	MPa	ISO 527-2/1A/1
Tensile Stress (Break, 23°C)	67.5	MPa	ISO 527-2/1A/5
Tensile Strain (Break, 23°C)	2.5	%	ISO 527-2/1A/5

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	4.5	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	17	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	102	°C	ISO 306/B50

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 5000 to 5500 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 65 to 70 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 2 to 3 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 15 to 19 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 4 to 5 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 100 to 104 °CDensity, ISO 1183: 1.15 to 1.17 g/cm³

Additional Information

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 5000 to 5500 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 65 to 70 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 2 to 3 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 15 to 19 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 4 to 5 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 100 to 104 °CDensity, ISO 1183: 1.15 to 1.17 g/cm³

Resin Grade	Manufacturer	Category	Trademark
Verolloy CGF10	PlastxWorld Inc.	PC+Acrylic	Verolloy
Zytel® HTN 51G45HSL BK083	DuPont Performance Polymers	PPA	Zytel® HTN
Chemical Resources HD07960	Chemical Resources, Inc.	HDPE	Chemical Resources
Evolue™ SP2540	Prime Polymer Co., Ltd.	LLDPE	Evolue™
Lucent PBT GPB-FR515	Lucent Polymers, Inc.	PBT	Lucent PBT