RTP 2099 X 141518 A
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MzYfRX_RTP2099X141518A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stainless Steel Fiber - Electrically Conductive - EMI/RFI Shielding - Flame Retardant - High Impact - (Preliminary Data Sheet) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.90 | % | ASTM D955 |
| Moisture Content | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay | sec | FTMS 101C 4046.1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2070 | MPa | ASTM D638 |
| Tensile Strength | 53.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 530 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 98.9 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | < 1.0E+4 | ohms | ESD STM11.11 |
| -- | < 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | < 10 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.5 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 - 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Dew Point | -29 | °C | |
| Processing (Melt) Temp | 243 - 271 | °C | |
| Mold Temperature | 60 - 93 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps.Remove hopper magnets.Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toraypef® 20020 AP17 | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| 4LOY® 25E17200 | 4Plas | PC+ABS | 4LOY® |
| Geon™ Duracap™ L4605 Red 7640 | PolyOne Corporation | PVC, Semi-Rigid | Geon™ Duracap™ |
| Kafrit PEX TA 2420 CL | Kafrit NA Ltd. | XLPE | Kafrit PEX |
| LNP™ LUBRICOMP™ RI001 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |