Vydyne® R530 NAT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MzW1bh_Vydyne-R530-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vydyne R530 NAT is general-purpose, injection-molding grade, 30% glass-fiber reinforced PA66 resin. Available in natural, it is lubricated for good machine feed, flow and mold release. Typical Applications/End Uses: To come |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 23°C, 2.00 mm | 0.90 | -- | % | |
| Flow : 23°C, 2.00 mm | 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.90 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10000 | 7400 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 195 | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | 5.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 9600 | 6000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 270 | 190 | MPa | ISO 178 |
| Poisson's Ratio (23°C) | 0.40 | -- | ISO 527 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 10 | 11 | kJ/m² | |
| 23°C | 11 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 65 | 80 | kJ/m² | |
| 23°C | 75 | 85 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 10 | 11 | kJ/m² | |
| 23°C | 12 | 13 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00 mm | 2.2E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 1.1E-4 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 120 | -- | °C | |
| 1.50 mm | 120 | -- | °C | |
| 3.00 mm | 120 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 85.0 | -- | °C | |
| 1.50 mm | 85.0 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 115 | -- | °C | |
| 1.50 mm | 120 | -- | °C | |
| 3.00 mm | 120 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (3.00 mm) | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 24 | -- | kV/mm | IEC 60243 |
| Arc Resistance (3.00 mm) | PLC 5 | -- | ASTM D495 | |
| Comparative Tracking Index (3.00 mm) | 600 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.750 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | -- | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.750 mm | PLC 4 | -- | ||
| 1.50 mm | PLC 4 | -- | ||
| 3.00 mm | PLC 4 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CERTENE™ PHI-35 | Muehlstein | PP Homopolymer | CERTENE™ |
| Grivory® GV-2H | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| ICORENE® Foam Products | ICO Polymers NA, A Division of A. Schulman | PE, Unspecified | ICORENE® |
| LEXAN™ FXE1414T resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Pibiflex® 6097 NERO900 | SO.F.TER. SPA | TPC-ET | Pibiflex® |