SAXATEC™ 6120
| Category: | AES , Acrylonitrile Ethylene Styrene |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXATEC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MzRcyx_SAXATEC-6120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAXATEC 6120 is a easy flowing, weatherable AES injection molding grade, characterized by high impact strength, high stiffness and good resistance to heat distortion. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Moisture Content 1 | < 0.20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 37.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 30 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 32 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 60 | kJ/m² | |
| 23°C | 100 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180 | ||
| -30°C | 60 | kJ/m² | |
| 23°C | 100 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2(1.8 MPa, Unannealed, 60.0 mm Span) | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 94.0 | °C | ISO 306/B50 |
| Ball Pressure Test (80°C, 2.00 mm) | Pass | IEC 60335-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | B130 |
| 2 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitalac® 5000S | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| TKC PA 6.6 | TKC Kunststoffe e.K. | Nylon 66 | TKC |
| ALCOM® PP 620/2 SV51-734MCO | ALBIS PLASTIC GmbH | PP Homopolymer | ALCOM® PP |
| DuraGrip® DGR 6240CL | Advanced Polymer Alloys | TPE | DuraGrip® |
| Plaslube® PA6 CF30 TL15 BK | Techmer Engineered Solutions | Nylon 6 | Plaslube® |