| 18% Borated Polyethylene (HDPE) |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 - 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2070 | MPa | ASTM D638 |
| Tensile Strength | 10.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 1930 | MPa | ASTM D790 |
| Flexural Strength | 13.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 76.7 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 65.6 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 177 - 227 | °C | |
| Mold Temperature | 21.1 - 65.6 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.103 - 0.172 | MPa | |
| Screw Speed | 100 - 250 | rpm | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 6.35 - 12.7 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Pack (Hold) Pressure: 65 to 75% of Injection PressureFill Time: 1.0 to 2.0 in/secPack (Hold) Time: 10 to 15 secCooling Time: As requiredFeed Throat: CooledNozzle Type: Reverse TaperCheck Type: Free FlowInjection Pressure: As Required |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rynite® RE5329 BK503 | DuPont Performance Polymers | PET | Rynite® |
| Sinvicomp SRF3707 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Vi-Chem PVC VSR87-80I | Vi-Chem Corporation | PVC, Rigid | Vi-Chem PVC |
| Trilene® HF2.0BM | Chandra Asri Petrochemical | PP Homopolymer | Trilene® |
| DAI-EL™ G-558 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |