Lupoy® 1261-03
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MyzTbK_Lupoy-1261-03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUPOY PC 1261-03 resin is designed for extrusion blow molding(EBM) and injection stretch blow molding(ISBM) products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. Two base colors available: Ultra blue B0786T & Ice blue W0992T |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 74 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2410 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 60.0 | MPa | |
| Break | 72.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 150 | % | |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 96.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance - Change in Haze 1 | 45 | % | ASTM D1004 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Average Extent of Burning | 3 | cm | ASTM D635 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 950 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256 | |
| Instrumented Dart Impact (23°C, Total Energy) | 94.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed, 4.00 mm | 146 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | 132 | °C | |
| 1.8 MPa, Annealed, 4.00 mm | 143 | °C | |
| Vicat Softening Temperature | 151 | °C | ASTM D1525 2 |
| Ball Indentation Temperature | > 125 | °C | IEC 60598-1 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 3.00 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 1.0E-3 | ASTM D150 | |
| Comparative Tracking Index (2.00 mm) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature 3(2.00 mm) | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 26 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 0.70 to 1.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 1000g, 500 cycles, CS-10F Wheel |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| 3 . | 5 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® EME-6710S | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| Vexel PBT B12GF30 FR | Custom Resins Group | PBT | Vexel |
| Evermore PUR SS-1665N | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| EUROPLEX® Film HC 99716 | Evonik Industries AG | PVDF+PMMA | EUROPLEX® Film |
| Lupol® HI5302RB | LG Chem Ltd. | TPO | Lupol® |