| EnviroPCABS 5010IM is a Polycarbonate + ABS (PC+ABS) product. It is available in North America. Primary characteristic: impact resistant. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 4.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 53.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 2240 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 530 | J/m | ASTM D256 |
| Gardner Impact | 36.2 | J | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 121 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA TW30 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Stat-Tech™ NN-40CF/000 NH FRV0 Natural | PolyOne Corporation | Nylon 66 | Stat-Tech™ |
| Chemlon® 204-13 GVNH BK083 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Dynaprene® VE3080A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| PERSTIR® N09K7000AE0 | A.D. Compound S.p.A. | PS (GPPS) | PERSTIR® |