LNP™ THERMOCOMP™ RC006XXH compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MwYQcc_LNP-THERMOCOMP-RC006XXH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RC006XXH is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare. Also known as: LNP* THERMOCOMP* Compound RC-1006 HC Product reorder name: RC006XXH |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.70 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 25200 | MPa | ASTM D638 |
| -- | 24800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 269 | MPa | ASTM D638 |
| Break | 267 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.1 | % | ASTM D638 |
| Break | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 20300 | MPa | ASTM D790 |
| -- 5 | 19000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 364 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 382 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C 7 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 8 | 64 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 7.60 | J | ASTM D3763 |
| -- | 2.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 262 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 261 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 257 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 257 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VINIKA® D3058 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | VINIKA® |
| APEX® RM 8220 | Teknor Apex Company | PVC, Rigid | APEX® |
| Shida 030E-1 | JINJIANG City SHIDA Plastic Fine Co., Ltd. | SBS | Shida |
| Sylvin 9058-90UV Black 214 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ CL001I compound | SABIC Innovative Plastics | PS (HIPS) | LNP™ LUBRICOMP™ |