Hifax TKC 123 X
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MwRmpy_Hifax-TKC-123-X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP/EPR-Blend, 30%mineralfilled, impact modified |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Shrinkage 1 | ISO 2554 | ||
| l | 0.30 | % | |
| q | 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1870 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 17.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 30 | % | ISO 527-2 |
| Flexural Modulus | 2050 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 3.5 | kJ/m² | |
| 23°C | 21 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow (-30 to 85°C) | 3.6E-5 | cm/cm/°C | DIN 53752 |
| Note Message | |
|---|---|
| 1 . | after 48 hr/RT at 40 bar, on plaques |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BESTPOLUX PCA65/01 | Triesa Plastics | PC+ABS | BESTPOLUX |
| Axiall PVC 8923 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| POLYfill PPH FX801020 | Polykemi AB | PP Homopolymer | POLYfill |
| Vipel® F774-APT-20 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| 3M™ Dyneon™ PTFE Compound TF 8914 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |