Lupol® LW4302
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mv89ct_Lupol-LW4302.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUPOL LW-4302 is reinforced with combination of glass-fiber and inorganic filler, this product is excellent in dimensional stability and distortion-resistant characteristics. LW-4302 is ideal for relatively long shape products and those demanding dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 68.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 5490 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 98.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 150 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 200 - 220 | °C | |
| Middle Temperature | 200 - 230 | °C | |
| Front Temperature | 210 - 230 | °C | |
| Nozzle Temperature | 210 - 240 | °C | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 40.0 - 90.0 | °C | |
| Injection Pressure | 29.4 - 118 | MPa | |
| Back Pressure | 0.490 - 3.92 | MPa | |
| Screw Speed | 40 - 60 | rpm |
| Injection instructions |
|---|
| Injection Pressure, secondary: 800 to 1000 kg/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC5-12B30 | Spartech Polycom | PP Homopolymer | Spartech |
| Zytel® RS LC2800 NC010 | DuPont Performance Polymers | Nylon, Unspecified | Zytel® RS |
| Hanwha Total PP NH54G | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Karina RED COLOR CONCENTRATE 42/165-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9067F3 Red 6270 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |