ACRYLITE® Resist ZK-D

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Cyro LLC
Trademark:	ACRYLITE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	MtXBIx_ACRYLITE-Resist-ZK-D.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

ACRYLITE® Resist ZK-D polymer is an amorphous, impact-modified thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA).

Typical properties of ACRYLITE® Resist acrylic polymers are:

high weather resistance

high light transmission

improved resistance to stress cracking

good melt flow rate

easy to color

The special properties of ACRYLITE® Resist ZK-D polymer are:

High impact/break resistance and strength

medium melt flow rate

medium heat resistance

Application:
Used for injection molded parts, extruded and co-extruded sheet and profiles.

General Information
Additive	Impact Modifier
Features	Amorphous Good Colorability Good Flow Good Weather Resistance High Clarity High Impact Resistance High Strength Impact Modified Medium Heat Resistance
Uses	Appliance Components Decorative Displays Household Goods Housings Lenses Lighting Applications Thin-walled Parts Writing Instruments
Agency Ratings	EC 1907/2006 (REACH)
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Coextrusion Extrusion Injection Molding Profile Extrusion Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.16	g/cm³	ASTM D792
Apparent Density	0.71	g/cm³	ASTM D1895
Melt Mass-Flow Rate (MFR) (230°C/3.8 kg)	5.8	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.30 to 0.60	%	ASTM D955
Water Absorption (Equilibrium)	< 0.30	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	33		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1590	MPa	ASTM D638
Tensile Strength	44.1	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	5.0	%
Break	40	%
Flexural Modulus	1590	MPa	ASTM D790
Flexural Strength	64.8	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
0°C, 6.35 mm	35	J/m
23°C, 6.35 mm	59	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)	87.8	°C	ASTM D648
Vicat Softening Temperature	93.9	°C	ASTM D1525
CLTE - Flow (0 to 100°C)	9.4E-5	cm/cm/°C	ASTM D696

Optical	Nominal Value	Unit	Test Method
Transmittance (3200 µm)	91.5	%	ASTM D1003
Haze (3200 µm)	1.0	%	ASTM D1003
Yellowness Index (3.20 mm)	0.30	YI	ASTM D1925

Resin Grade	Manufacturer	Category	Trademark
Riblene® FC 40 F	Versalis S.p.A.	LDPE	Riblene®
Polylink Polymer PBT-11030-GF	Polylink Polymers (India) Ltd.	PBT	Polylink Polymer
Abstron SE-22M	Bhansali Engineering Polymers Limited	ABS	Abstron
Lifoflex® UV FLAM 40600	Müller Kunststoffe GmbH	TPE	Lifoflex®
Karina OCHER PVC COMPOUND 810-37/3-CRB	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina