Halene L 71601W
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene L |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MtRmey_Halene-L-71601W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
71601W is a LLDPE blown film grade produced by Spherilene Technology with controlled morphology, excellent processability and mechanical properties. This Grade can be used in General Purpose Adhesive Lamination film. 71601W is without slip additives and antiblock. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.916 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 15.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 13.0 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 30.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 21.0 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 650 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 850 | % | ASTM D882 |
| Dart Drop Impact 4(25 µm, Blown Film) | 100 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 120 | g | ASTM D1922 |
| TD : 25 µm, blown film | 440 | g | ASTM D1922 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°, 25.0 µm, Blown Film) | 90 | ASTM D2457 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 - 200 | °C | |
| Cylinder Zone 2 Temp. | 180 - 200 | °C | |
| Cylinder Zone 3 Temp. | 180 - 200 | °C | |
| Cylinder Zone 4 Temp. | 180 - 200 | °C | |
| Cylinder Zone 5 Temp. | 180 - 200 | °C | |
| Melt Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| Blow up Ratio: 2.0-3.0Die Gap: 2.0-2.5 mm |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | 38 mm Dart, 66 cm Height |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AESNO P40 TL | Arkema | Nylon 12 | Rilsamid® |
| TULAMID® PA-SV20-AP | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| ALTECH® POM A 1000/106 | ALBIS PLASTIC GmbH | Acetal (POM) Copolymer | ALTECH® POM |
| CoREZYN® CORVE8180 | Interplastic Corporation | Vinyl Ester | CoREZYN® |
| SQUARE® SSR8630-28AF/BF | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |