| Category: | PMP Copolymer , Polymethylpentene Copolymer |
| Manufacturer: | Mitsui Chemicals, Inc. |
| Trademark: | TPX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mt5GUn_TPXMX004XB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TPX®MX004XB is a polymethylpentene copolymer (PMP copolymer) material,. This product is available in North America. The processing methods are: film extrusion, blow molding, extrusion, fiber (spinning) extrusion or injection molding. TPX®The main features of the MX004XB are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.833 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 25 | g/10 min | ASTM D1238 |
| Spiral Flow 1 | 53.0 | cm | Internal method |
| Molding Shrinkage 2 | Internal method | ||
| Flow | 1.5 | % | Internal method |
| Transverse flow | 1.1 | % | Internal method |
| Water Absorption (24 hr) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 75 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1300 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 25.0 | MPa | ASTM D638 |
| Fracture, 23°C | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 30 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1050 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 32.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 24 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 40 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 100 | °C | ASTM D648 |
| Vicat Softening Temperature | 165 | °C | ASTM D1525 |
| Melting Temperature | 228 | °C | DSC |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 65 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.10 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.460 | ASTM D542 | |
| Transmittance | 94.0 | % | ASTM D1003 |
| Haze | 0.70 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Mold temperature: 73°C, melt temperature: 310 to 320°C |
| 2 . | temperature range: 260 to 280°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIKASUPER® LCP E7006L | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Wondel® B BN0 | Nanjing Julong Engineering Plastics Co., LTD | Nylon 6 | Wondel® B |
| Evoprene™ GC 645 | AlphaGary | SEBS | Evoprene™ GC |
| ECONAMID® 6GB30FL | DOMO Engineering Plastics SPA | Nylon 6 | ECONAMID® |
| Geon™ Vinyl Wire & Cable WJMS800 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |