| Plexiglas® MI7G is an impact modified thermoplastic acrylic resin formulated for injection molding and extrusion applications.This grade is formulated for approved medical applications and has improved gamma resistance compared to MI7. It is heat resistant, has high melt flow and provides 7 times the impact resistance of standard acrylics while maintaining excellent optical properties. It offers an excellent balance between melt flow and increased resistance to breakage, while providing weatherability superior to that provided by other high-impact plastics. Supplemental moldflow simulation data is available. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 68 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2520 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 48.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 35 | % | ASTM D638 |
| Flexural Modulus | 2380 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 77.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 91.1 | °C | |
| 1.8 MPa, Annealed | 85.0 | °C | |
| Vicat Softening Temperature | |||
| -- | 98.9 | °C | ASTM D1525 2 |
| -- | 90.0 | °C | ASTM D1525 3 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 4 | 1.490 | ASTM D542 | |
| Transmittance (3180 µm) | 91.0 | % | ASTM D1003 |
| Haze (3180 µm) | < 2.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ASTM Classification | PMMA 0221V3 | ASTM D788 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.30 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 216 to 238 | °C | |
| Middle Temperature | 216 to 238 | °C | |
| Front Temperature | 216 to 238 | °C | |
| Nozzle Temperature | 216 to 238 | °C | |
| Processing (Melt) Temp | 238 | °C | |
| Mold Temperature | 37.8 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | Annealing cycle: 4hrs @ 176°F |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| 4 . | ND @ 72°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ C16USQM42 | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| S&E PVC GA-1006 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| NEOFLON™ NP-120 | DAIKIN AMERICA, INC. | FEP | NEOFLON™ |
| Daplen™ EF210AE | Borealis AG | PP, Unspecified | Daplen™ |
| Jampilen EP540P | Jam Polypropylene Company | PP Copolymer | Jampilen |