Edgetek™ PC-20GF/000
| Category: | PC , Polycarbonate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MsNyBO_Edgetek-PC-20GF-000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Edgetek™ PC-20GF/000 is a Polycarbonate (PC) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 to 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 6890 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 107 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 5520 | MPa | ASTM D790 |
| Flexural Strength | 131 | MPa | ASTM D790 |
| Compressive Strength | 141 | MPa | ASTM D695 |
| Shear Strength | 58.6 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm, Injection Molded) | 130 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed, 3.18 mm | 149 | °C | |
| 1.8 MPa, Annealed, 3.18 mm | 143 | °C | |
| CLTE - Flow | 2.9E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.34 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 82.2 to 121 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4PROP® 9C23200 | 4Plas | PP Copolymer | 4PROP® |
| APEX® RE 9018 | Teknor Apex Company | PVC, Rigid | APEX® |
| Karina GRAY PVC COMPOUND 751-18/355-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| NILAMID® XS3 GF55 TF10 | Nilit Plastics | Nylon, Unspecified | NILAMID® |
| DAI-EL™ G-101 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |