Order Products : sales@su-jiao.com
Ghaed ABS ABS-HFA-70
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Ghaed Basir Petrochemicals Co. |
| Trademark: | Ghaed ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MrXVsV_Ghaed-ABS-ABS-HFA-70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Classification: General grade ABS>Flame retardant Characteristic: medium Impact Strength > Flame retardant Application: Electrical and Electronic part s,TV,VTR,Printer,facsmilie,computer,monitor&requiring flame retardant property. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 40 to 50 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 to 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 23°C) | > 41.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C) | > 18 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | > 1770 | MPa | ASTM D790 |
| Flexural Strength 4(23°C) | > 61.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 5 | > 18 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 82.0 | °C | ASTM D648 |
| Vicat Softening Temperature | > 93.0 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 160 to 170 | °C | |
| Middle Temperature | 170 to 190 | °C | |
| Front Temperature | 190 to 200 | °C | |
| Nozzle Temperature | 195 to 205 | °C | |
| Processing (Melt) Temp | 210 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 6.4mm |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 4080 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| FHR Polypropylene P6G2Z-090 | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Iupiace® LN23 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| Lupoy® GN2101FC | LG Chem Ltd. | PC | Lupoy® |
| Durethan® BM 40 X H3.0 EF 000000 | LANXESS GmbH | Nylon 6 | Durethan® |