Capran® 526

Category:	Nylon, Unspecified , Polyamide
Manufacturer:	Honeywell
Trademark:	Capran®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Mr6sXc_Capran-526.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
CAPRAN® 526 is a blue tinted, heat-stabilized blown film produced from modified nylon resin. It is available in widths up to 60 inches as layflat tubing and 120 inches as slit tubing. Thicknesses are 2.0 and 3.0 mils. Blown film is recommended as bagging film for advanced composite fabrication and other high temperature applications where softness, workability or anti-static characteristics are essential. In addition, CAPRAN® 526 has excellent heat stability and resistance to pinholing and can be used at temperatures up to 450°F (232°C) for typical composite cure cycle times.

Message

CAPRAN® 526 is a blue tinted, heat-stabilized blown film produced from modified nylon resin. It is available in widths up to 60 inches as layflat tubing and 120 inches as slit tubing. Thicknesses are 2.0 and 3.0 mils. Blown film is recommended as bagging film for advanced composite fabrication and other high temperature applications where softness, workability or anti-static characteristics are essential. In addition, CAPRAN® 526 has excellent heat stability and resistance to pinholing and can be used at temperatures up to 450°F (232°C) for typical composite cure cycle times.

General Information
Additive	Antistatic property heat stabilizer
Features	Antistatic property Workability, good Thermal Stability Thermal stability, good Soft
Uses	Films
Appearance	Transparent-Light Blue
Forms	Films

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	51	µm
Secant Modulus - MD (51 µm)	517	MPa	ASTM D882
Tensile Strength - MD			ASTM D882
Yield, 51 µm	34.5	MPa	ASTM D882
Break, 51 µm	103	MPa	ASTM D882
Tensile Elongation - MD (Break, 51 µm)	400	%	ASTM D882
Elmendorf Tear Strength - MD (51 µm)	100	g	ASTM D1922

Thermal	Nominal Value	Unit	Test Method
Peak Crystallization Temperature (DSC)	257 - 259	°C	ASTM D3418

Additional Information
Dimensional Stability, ASTM D1204, 30 mins, 300°F: <1% shrinkage

Resin Grade	Manufacturer	Category	Trademark
Small Boss SPVC001	Tongxiang Small Boss Special Plastic Products Co., Ltd.	PVC, Flexible	Small Boss
Staramide AST42K	Eurostar Engineering Plastics	Nylon 66	Staramide
Beetle® PBTS120S	Teknor Apex Company (Chem Polymer)	PBT	Beetle®
Chemical Resources HD2955	Chemical Resources, Inc.	HDPE	Chemical Resources
Durethan® AKV 50 H3.0 000000	LANXESS GmbH	Nylon 66	Durethan®