40 Shore D High Performance Polyester Elastomer

General Information
Additive	UV Stabilizer
Uses	Film Profiles Sheet
Agency Ratings	UL Unspecified Rating
Forms	Pellets
Processing Method	Calendering Casting Coating Extrusion Film Extrusion Injection Molding Profile Extrusion Sheet Extrusion Thermoforming
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (TPE) (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) Tensile Modulus vs. Temperature, Dynamic (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
Part Marking Code (ISO 11469)	>TPC-ET<
Resin ID (ISO 1043)	TPC-ET

Physical	Nominal Value	Unit	Test Method
Density	1.16	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	5.6	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)	5.00	cm³/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Across Flow	0.40	%
Flow	0.20	%
Water Absorption
24 hr	0.60	%	ASTM D570
23°C, 24 hr, 2.00 mm	0.70	%	ISO 62
Equilibrium, 23°C, 2.00 mm, 50% RH	0.20	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Shore Hardness			ISO 868
Shore D	43
Shore D, 15 sec	37

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	60.0	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Break	26.0	MPa
5.0% Strain	2.40	MPa
10% Strain	4.60	MPa
50% Strain	8.40	MPa
Tensile Strain (Break)	> 300	%	ISO 527-2
Nominal Tensile Strain at Break	500	%	ISO 527-2
Tensile Creep Modulus			ISO 899-1
1 hr	54.0	MPa
1000 hr	40.0	MPa
Flexural Modulus	64.0	MPa	ISO 178
Abrasion Resistance	200	mm³	ISO 4649

Additional Information	Nominal Value	Unit
Effective Thermal Diffusivity	0.0544	cSt

Elastomers	Nominal Value	Unit	Test Method
Tear Strength			ISO 34-1
Across Flow	96	kN/m
Flow	100	kN/m

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-40°C	No Break
-30°C	No Break
23°C	No Break
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	No Break
23°C	No Break
Notched Izod Impact Strength			ISO 180/1A
-40°C	No Break
23°C	No Break
Tensile Impact Strength (23°C)	230	kJ/m²	ISO 8256/1

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	-97.0	°C	ISO 974
Glass Transition Temperature ¹	-50.0	°C	ISO 11357-2
Melting Temperature ²	152	°C	ISO 11357-3
CLTE			ISO 11359-2
Flow	1.3E-4	cm/cm/°C
Transverse	1.6E-4	cm/cm/°C

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	2.0E+14	ohms	IEC 60093
Volume Resistivity	7.0E+12	ohms·cm	IEC 60093
Electric Strength	18	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
100 Hz	5.20
1 MHz	4.70
Dissipation Factor			IEC 60250
100 Hz	0.011
1 MHz	0.053
Comparative Tracking Index	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flammability Classification (1.50 mm)	HB		IEC 60695-11-10, -20
Oxygen Index	20	%	ISO 4589-2

Fill Analysis	Nominal Value	Unit
Melt Density	1.02	g/cm³

Note Message
1 .	10°C/min
2 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
AMTOPP AA40	Inteplast Group	PP, Unspecified	AMTOPP
ECP 115	TBA Electro Conductive Products Ltd.	PP, Unspecified	ECP
Hifax EKC 107X	LyondellBasell Industries	PP Copolymer	Hifax
INSPIRE™ 153	Braskem Europe GmbH	PP Impact Copolymer	INSPIRE™
Techsil® RTV27909	Techsil Limited	Silicone Rubber, RTV-2	Techsil®